HDPE SNOLEN® IM 13/56 E JSC Gazprom neftekhim Salavat
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® IM 13/56 E |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 3.0 kJ/m² |
| hardness | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® IM 13/56 E |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 62 |
| Mechanical properties | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® IM 13/56 E |
|---|---|---|---|
| fracture | ISO 527-2/50 | >1000 % | |
| yield | ISO 527-2 | 10 % | |
| Tensile modulus | 23°C，正割 | ISO 527-2/1 | 1100 MPa |
| tensile strength | 屈服 | ISO 527-2/50 | 26.0 MPa |
| 断裂 | ISO 527-2/50 | 30.0 MPa |
| physical property | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® IM 13/56 E |
|---|---|---|---|
| density | 23°C | ISO 1183 | 0.952to0.956 g/cm³ |
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 9.0to13 g/10min |
| Melt flow ratio | 2.30to3.30 | ||
| Environmental stress cracking resistance | 80°C,2%Arkopal | ISO 16770 | 3.00 hr |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 3.5to5.0 g/10min |
| Thermal performance | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® IM 13/56 E |
|---|---|---|---|
| vicat | ISO 306/B50 | 70.0 °C | |
| brittle temperature | ASTM D746 | <-80.0 °C |