PC DX11354X SABIC INNOVATIVE NANSHA
LEXAN™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11354X |
|---|---|---|---|
| 23°C | ISO 180/1A | 60 kJ/m² | |
| ASTM D256 | 700 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11354X |
|---|---|---|---|
| yield | ASTM D638 | 55.0 Mpa | |
| ASTM D638 | 5.0 % | ||
| ISO 527-2/50 | 54.0 Mpa | ||
| Yield, 50.0mm span | ASTM D790 | 86.0 Mpa | |
| fracture | ISO 527-2/50 | 51.0 Mpa | |
| ASTM D638 | 45.0 Mpa | ||
| ISO 527-2/50 | 84 % | ||
| ASTM D638 | 70 % | ||
| yield | ISO 527-2/50 | 5.0 % | |
| --8 | ISO 178 | 86.0 Mpa | |
| 50.0mm span | ASTM D790 | 2380 Mpa | |
| --1 | ASTM D638 | 2400 Mpa | |
| --7 | ISO 178 | 2450 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11354X |
|---|---|---|---|
| dielectric constant | 1.00GHz | ASTM D150 | 3.03 |
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms | |
| Dissipation Factor | 1.00GHz | ASTM D150 | 6.6E-03 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11354X |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.50-0.70 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 20.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
| Shrinkage rate | TD:24小时 | ISO 294-4 | 0.50-0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX11354X |
|---|---|---|---|
| vicat | ISO 306/B50 | 136 °C | |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7.1E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 117 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 121 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 6.5E-05 cm/cm/°C |