Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA BKV 215 H2.0 901510 LANXESS GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/BKV 215 H2.0 901510 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 65 kJ/m² |
| 23°C | ISO 180/1U | 60 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 4.50 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 11.0 J |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 1440 N |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 20 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 80 kJ/m² |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 775 N |
| hardness | Test Condition | Test Method | LANXESS GERMANY/BKV 215 H2.0 901510 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 120 MPa |
| Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/BKV 215 H2.0 901510 |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA6/66-HI.GHR.14-040.GF15 |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/BKV 215 H2.0 901510 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 4.5 % |
| bending strength | 23°C4 | ISO 178/A | 135 MPa |
| Bending Strain | 23°C | ISO 178/A | 5.5 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 85.0 MPa |
| Tensile modulus | 23°C | ISO 527-2/1 | 4500 MPa |
| Flexural modulus | 23°C | ISO 178/A | 4200 MPa |
| bending strength | 3.5%Strain,23°C | ISO 178/A | 125 MPa |
| flammability | Test Condition | Test Method | LANXESS GERMANY/BKV 215 H2.0 901510 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| Limiting Oxygen Index | ISO 4589-2 | 22 % | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LANXESS GERMANY/BKV 215 H2.0 901510 |
|---|---|---|---|
| Shrinkage rate | MD:120°C,4小时,2.00mm3 | ISO 2577 | 0.10 % |
| TD:280°C,2.00mm2 | ISO 2577 | 0.60 % | |
| density | 23°C | ISO 1183 | 1.17 g/cm³ |
| Shrinkage rate | MD:280°C,2.00mm2 | ISO 2577 | 0.60 % |
| Apparent density | ISO 60 | 0.60 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.0 % |
| 饱和,23°C | ISO 62 | 7.0 % | |
| Shrinkage rate | TD:120°C,4小时,2.00mm3 | ISO 2577 | 0.10 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/BKV 215 H2.0 901510 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 214 °C | |
| vicat | ISO 306/B120 | 200 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 205 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 1.7E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 175 °C |
| 8.0MPa,未退火，HDT | ISO 75-2/C | 60.0 °C |