PPO(PPE)+TPE NORYL™ WCP921 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC/NORYL™ WCP921 resin |
|---|---|---|---|
| Shore hardness | 邵氏A,30秒 | ASTM D2240 | 88 |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL™ WCP921 resin |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 150 % |
| tensile strength | 断裂 | ASTM D638 | 15.0 MPa |
| Flexural modulus | 100mmSpan | ASTM D790 | 180 MPa |
| ISO 178 | 200 MPa | ||
| Tensile strain | 断裂 | ISO 527-2/50 | 140 % |
| tensile strength | 断裂 | ISO 527-2/50 | 15.0 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/NORYL™ WCP921 resin |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | ASTM D257 | 7.1E+15 ohms·cm | |
| dielectric strength | 2.00mm,inOil | IEC 60243-1 | 25 kV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.80 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.029 |
| flammability | Test Condition | Test Method | SABIC/NORYL™ WCP921 resin |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 850 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 725 °C |
| UL flame retardant rating | 6.0mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 24 % |
| physical property | Test Condition | Test Method | SABIC/NORYL™ WCP921 resin |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 17 g/10min |
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.55 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.060 % |
| density | ASTM D792 | 1.04 g/cm³ | |
| melt mass-flow rate | 210°C/5.0kg | ASTM D1238 | 15 g/10min |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.65 % |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL™ WCP921 resin |
|---|---|---|---|
| brittle temperature | ASTM D746 | <-40.0 °C |