Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO SE1X-GY6C258 SABIC INNOVATIVE SHANGHAI
NORYL™ 
Electronic and electrical、Mechanical component cove、Household products
High temperature resistan、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SE1X-GY6C258
Dart impact-30°C, Energy at PeakASTM D376332.0 J
23°C, Energy at PeakASTM D376351.0 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SE1X-GY6C258
elongation断裂ASTM D63820 %
屈服ASTM D6388.1 %
tensile strength 断裂ASTM D63853.0 Mpa
bending strength屈服, 100 mm 跨距ASTM D790102 Mpa
tensile strength 屈服ASTM D63867.0 Mpa
Flexural modulus100 mm 跨距ASTM D7902500 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SE1X-GY6C258
dielectric strength3.20 mm, in OilASTM D14918 KV/mm
Volume resistivityASTM D2572.3E+16 ohms·cm
Surface ResistivityASTM D257> 1.0E+15 ohms
dielectric constant60 HzASTM D1502.52
Dissipation Factor60 HzASTM D1503.4E-3
50 HzASTM D1503.4E-3
dielectric constant1 MHzASTM D1502.46
arc resistanceASTM D495PLC 6
High Voltage Arc Traceability Rate (HVTR)UL 746PLC 4
Compared to the Leakage Tracking Index (CTI)UL 746PLC 1
Dissipation Factor1 MHzASTM D1502.1E-3
dielectric constant50 kHzASTM D1502.52
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SE1X-GY6C258
UL flame retardant rating6.0 mmUL 94V-0
1.5 mmUL 94V-1
Radiation board gradeRP100
physical property Test ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SE1X-GY6C258
Shrinkage rate横向流动 2内部方法0.50 - 0.70 %
Outdoor applicabilityUL 746Cf1
Water absorption rate24 hrASTM D5700.060 %
Shrinkage rate流动 : 3.20 mm内部方法0.50 - 0.70 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SE1X-GY6C258
Heat distortion temperature1.8 MPa, 未退火, 6.40 mm，HDTASTM D648117 °C
RTI ImpUL 746105 °C
RTIUL 746110 °C
Heat distortion temperature0.45 MPa, 未退火, 6.40 mm，HDTASTM D648126 °C
RTI ElecUL 746110 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/SE1X-GY6C258
drying time3.0 to 4.0 hr
screw speed20 to 100 rpm
Suggested maximum moisture content0.020 %
Temperature in the middle of the barrel260 to 305 °C
Temperature at the rear of the barrel250 to 300 °C
Processing (melt) temperature280 to 310 °C
drying temperature105 to 110 °C
Suggested injection volume30 to 70 %
Temperature at the front of the material cylinder270 to 310 °C
Back pressure0.300 to 0.700 Mpa
Temperature75 to 105 °C
Spray nozzle temperature280 to 310 °C