Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PET 415HP-NC010 DUPONT JAPAN
Rynite®
Fitness equipment、Automotive Applications
High impact resistance、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT JAPAN/415HP-NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
| -30°C | ISO 179/1eU | 25 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT JAPAN/415HP-NC010 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 111 |
| M计秤 | ISO 2039-2 | 58 |
| Mechanical properties | Test Condition | Test Method | DUPONT JAPAN/415HP-NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 4700 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 5.0 % |
| Flexural modulus | ISO 178 | 3550 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 79.0 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT JAPAN/415HP-NC010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| flammability | Test Condition | Test Method | DUPONT JAPAN/415HP-NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94,IEC60695-11-10,-20 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 19 % | |
| UL flame retardant rating | 1.5mm | UL 94,IEC60695-11-10,-20 | HB |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT JAPAN/415HP-NC010 |
|---|---|---|---|
| Shrinkage rate | MD3 | ISO 294-4 | 0.50 % |
| Melt volume flow rate | 280°C/2.16kg | ISO 1133 | 4.00 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 2.5 % |
| Shrinkage rate | TD3 | ISO 294-4 | 1.2 % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.25 % |
| Thermal performance | Test Condition | Test Method | DUPONT JAPAN/415HP-NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 250 °C | |
| Linear coefficient of thermal expansion | MD:-40到23°C | ISO 11359-2 | 9.8E-05 cm/cm/°C |
| TD:55到160°C | ISO 11359-2 | 3.2E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 235 °C |
| vicat | ISO 306/B50 | 205 °C | |
| Linear coefficient of thermal expansion | TD:-40到-23°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 207 °C |
| Linear coefficient of thermal expansion | MD:55到160°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| EffectiveThermalDiffusivity | ISO 11359-2 | 9E-08 m²/s | |
| MD | ISO 11359-2 | 2E-05 cm/cm/°C | |
| TD | ISO 11359-2 | 1.2E-04 cm/cm/°C |