PC/ABS C1200HF-100 SABIC INNOVATIVE CHONGQING

CYCOLOY™

Electrical field,Electronic field,Automotive interior parts

High impact resistance,heat-resisting

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C1200HF-100
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	129 °C
Hot deformation temperature		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	112 °C
Linear coefficient of thermal expansion	-40 to 40°C，Flow	ASTM E831	7.2E-5 cm/cm/°C
RTI		UL 746	105 °C
RTI Elec		UL 746	105 °C
RTI Imp		UL 746	80.0 °C
Vicat softening temperature		ISO 306/B50	130 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C1200HF-100
Bending modulus	50.0 mm Span	ASTM D790	2340 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	88.0 Mpa
elongation	Yield	ASTM D638	5.0 %
elongation		Break	ASTM D638	100 %
Tensile modulus		ASTM D638	2270 Mpa
tensile strength	Yield	ASTM D638	57.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C1200HF-100
Compared to the anti leakage trace index		UL 746	PLC 2
High arc combustion index		UL 746	PLC 1
Hot wire ignition		UL 746	PLC 3

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C1200HF-100
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	19 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C1200HF-100
Dart impact	-30°C, Total Energy	ASTM D3763	54.0 J
Dart impact		23°C, Total Energy	ASTM D3763	54.0 J

flammability	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C1200HF-100
UL flame retardant rating	1.2 mm	UL 94	HB

injection	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C1200HF-100
Back pressure			0.300 to 0.700 Mpa
drying temperature			100 to 110 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.038 to 0.076 mm
Hopper temperature			60 to 80 °C
Mold temperature			60 to 90 °C
Processing (melt) temperature			275 to 300 °C
Screw speed			40 to 70 rpm
Spray nozzle temperature			275 to 300 °C
Suggested injection volume			30 to 80 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			260 to 300 °C
Temperature at the rear of the barrel			250 to 290 °C
Temperature in the middle of the barrel			255 to 295 °C