Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 2081-15 STYRON US
CALIBRE™ MEGARAD™
Medical supplies、Nursing supplies
Medical grade
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | STYRON US/2081-15 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | SK | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ASTMD256 | 无断裂 |
| Dart impact | 23°C,总能量 | ASTM D3763 | 81.3 J |
| Impact strength of cantilever beam gap | ASTM D1822 | 378 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | SK | 无断裂 |
| hardness | Test Condition | Test Method | STYRON US/2081-15 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | STYRON US/2081-15 |
|---|---|---|---|
| elongation | 断裂5 | ASTM D638 | 150 % |
| tensile strength | 屈服5 | ASTM D638 | 62.1 Mpa |
| Tensile modulus | -- | ISO 527-2/50 | 2300 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 150 % |
| Tensile modulus | --5 | ASTM D638 | 2210 Mpa |
| Abrasion | ASTM D1044 | 45 % | |
| Flexural modulus | --7,8 | ISO 178 | 2400 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 68.0 Mpa |
| bending strength | --6 | ASTM D790 | 96.5 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 62.0 Mpa |
| elongation | 屈服 | ISO 527-2/50 | 6.0 % |
| bending strength | --7,8 | ISO 178 | 98.0 Mpa |
| elongation | 屈服5 | ASTM D638 | 6.0 % |
| 断裂 | ISO 527-24 | >50 % | |
| tensile strength | 断裂5 | ASTM D638 | 68.3 Mpa |
| Flexural modulus | --6 | ASTM D790 | 2410 Mpa |
| Electrical performance | Test Condition | Test Method | STYRON US/2081-15 |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 1E-03 |
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| 100Hz | IEC 602504 | 3.00 | |
| 1MHz | ASTMD150 | 3.00 | |
| Dissipation Factor | 100Hz | IEC 602504 | 1E-03 |
| Volume resistivity | -- | ASTM D257 | 2E+17 ohms·cm |
| Dissipation Factor | 1MHz | ASTMD150 | 2E-03 |
| Volume resistivity | -- | IEC 600934 | >1.0E+13 ohms·m |
| dielectric strength | ASTMD1494 | 17 KV/mm |
| optical performance | Test Condition | Test Method | STYRON US/2081-15 |
|---|---|---|---|
| refractive index | ASTMD542 | 1.586 | |
| transmissivity | ASTM D1003 | 89.0 % | |
| Haze ratio | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | STYRON US/2081-15 |
|---|---|---|---|
| UL flame retardant rating | 3.20mm | ISO 12104 | HB |
| Normal combustion performance with a thickness of 1.6mm | 1.60mm,UL | ISO 12104 | HB |
| physical property | Test Condition | Test Method | STYRON US/2081-15 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ASTMD570 | 0.32 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 11334 | 12.0 cm3/10min |
| Shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| MD | ISO 294-4 | 0.50-0.70 % | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.15 % |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON US/2081-15 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 122 °C |
| vicat | 50°C/h,B(50N) | ISO 3064 | 143 °C |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-24 | 137 °C |
| vicat | -- | ASTM D152510 | 148 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTM D648 | 136 °C |
| 1.8MPa，HDT | ISO 75-24 | 123 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 120 °C | |
| vicat | -- | ISO 306/B50 | 143 °C |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ASTM D648 | 139 °C |
| Linear coefficient of thermal expansion | MD：-- | ISO 178/1993 | 7E-05 cm/cm/°C |