Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM N2320 0038 AT BASF KOREA
Ultraform®
Automotive Applications、Toy
High impact resistance、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | BASF KOREA/N2320 0038 AT |
|---|---|---|---|
| Limiting Oxygen Index | 15 % | ||
| loss angle | 100HZ | 10 |
| Basic performance | Test Condition | Test Method | BASF KOREA/N2320 0038 AT |
|---|---|---|---|
| Water absorption rate | 0.8 % | ||
| density | 1400 kg/cm | ||
| melt mass-flow rate | 220℃/10kg | 7.5 CM |
| Electrical performance | Test Condition | Test Method | BASF KOREA/N2320 0038 AT |
|---|---|---|---|
| dielectric strength | 40 KV/mm | ||
| dielectric constant | 100HZ | 3.8 | |
| Surface Resistivity | 1E+13 Ohm | ||
| Volume resistivity | 1E+13 Ohm |
| Mechanical properties | Test Condition | Test Method | BASF KOREA/N2320 0038 AT |
|---|---|---|---|
| Charpy Notched Impact Strength | 23℃ | 5.5 KJ/m | |
| Tensile modulus | 2600 Mpa | ||
| 1h | 1800 Mpa | ||
| elongation at yield | 9.6 % | ||
| tensile strength | 屈服 | 63 Mpa | |
| elongation | 断裂 | 29 % |
| physical property | Test Condition | Test Method | BASF KOREA/N2320 0038 AT |
|---|---|---|---|
| Shrinkage rate | 水平方向 | 2.1 % |
| Thermal performance | Test Condition | Test Method | BASF KOREA/N2320 0038 AT |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa，HDT | 105 °C | |
| Linear coefficient of thermal expansion | 水平方向 | 1.1 E-4/℃ | |
| vicat | 50℃/h50n | 150 °C | |
| burning rate | 1.6mm | HB CLASS | |
| melting temperature | 10℃/min | 167 °C |