Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA4T F11 DSM HOLAND
ForTii®
Electronic and electrical
Thermal stability、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/F11 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/F11 |
|---|---|---|---|
| Tensile modulus | -- | ISO 527-2 | 12000 Mpa |
| Tensile stress | 断裂 | ISO 527-2 | 155 Mpa |
| Bending stress | ISO 178 | 245 Mpa | |
| Tensile strain | 断裂, 120°C | ISO 527-2 | 2.7 % |
| Tensile stress | 断裂, 120°C | ISO 527-2 | 100 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Flexural modulus | ISO 178 | 11500 Mpa | |
| Tensile strain | 断裂, 160°C | ISO 527-2 | 3.7 % |
| Tensile stress | 断裂, 160°C | ISO 527-2 | 70.0 Mpa |
| Tensile modulus | 160°C | ISO 527-2 | 5000 Mpa |
| 120°C | ISO 527-2 | 7500 Mpa |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/F11 |
|---|---|---|---|
| CTI | IEC 60112 | 600 V | |
| dielectric strength | IEC 60243-1 | 33 KV/mm | |
| 1 MHz | IEC 60250 | 3.90 | |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| 1.00 GHz | IEC 60250 | 3.90 | |
| 10.0 GHz | IEC 60250 | 3.90 | |
| 100 Hz | IEC 60250 | 4.20 |
| flammability | Test Condition | Test Method | DSM HOLAND/F11 |
|---|---|---|---|
| Flammability level | 0.200 mm | IEC 60695-11-10, -20 | V-0 |
| 1.5 mm | IEC 60695-11-10, -20 | V-0 |
| physical property | Test Condition | Test Method | DSM HOLAND/F11 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.6 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
| 横向流量 | ISO 294-4 | 1.2 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/F11 |
|---|---|---|---|
| 流动 | ISO 11359-2 | 1.5E-5 3.0E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 3.5E-5 7.0E-5 cm/cm/°C | |
| RTI Elec | 0.35 mm | UL 746 | 140 °C |
| Thermal Index - 5000 hr | IEC 60216 | 163 °C | |
| Melting temperature 3 | ISO 11357-3 | 325 °C | |
| 1.8 MPa, 未退火 | ISO 75-2/A | 305 °C |