PC 8600-20 IC7700178 STYRON TAIWAN
EMERGE™
Electrical enclosure、Electronic field、Electrical field、Electrical/Electronic App
Flame retardant、High mobility、Bromine free
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | STYRON TAIWAN/8600-20 IC7700178 |
|---|---|---|---|
| Rockwell hardness | R-Scale,4.00mm | ISO2039-2 | 123 |
| Mechanical properties | Test Condition | Test Method | STYRON TAIWAN/8600-20 IC7700178 |
|---|---|---|---|
| TensileStrain | Yield,4.00mm,InjectionMolded | ISO527-2/50 | 6.0 % |
| Tensile strain | 断裂,4.00mm,注塑 | ISO527-2/50 | 100 % |
| Bending modulus 2 | 4.00mm,InjectionMolded | ISO178 | 2400 Mpa |
| tensile strength | Yield,4.00mm,InjectionMolded | ISO527-2/50 | 60.0 Mpa |
| Tensile stress | 断裂,4.00mm,注塑 | ISO527-2/50 | 58.0 Mpa |
| Bending strength 2 | 4.00mm,InjectionMolded | ISO178 | 94.0 Mpa |
| flammability | Test Condition | Test Method | STYRON TAIWAN/8600-20 IC7700178 |
|---|---|---|---|
| Extreme Oxygen Index 3 | ISO4589-2 | 35 % | |
| FlameRating3 | 1.5mm | UL94 | V-0 |
| GlowWireIgnitionTemperature3 | 1.0mm | IEC60695-2-13 | 960 °C |
| physical property | Test Condition | Test Method | STYRON TAIWAN/8600-20 IC7700178 |
|---|---|---|---|
| Shrinkage rate | ISO294-4 | 0.50to0.70 % | |
| melt mass-flow rate | 300°C/1.2kg | ISO1133 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON TAIWAN/8600-20 IC7700178 |
|---|---|---|---|
| vicat | -- | ISO306/A120 | 150 °C |
| 0.45MPa,未退火 | ISO75-2/B | 136 °C | |
| RTI Str | UL746 | 125 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 122 °C | |
| RTI Elec | UL746 | 125 °C | |
| IEC60335-1 | >125 °C | ||
| MD：-40到82°C | ASTMD696 | 6.5E-05 cm/cm/°C | |
| vicat | -- | ISO306/B50 | 143 °C |
| RTI Imp | UL746 | 125 °C |