Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 MT409AHS NC010 DUPONT USA
Zytel®
Electrical appliances
Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/MT409AHS NC010 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 19 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 13 kJ/m² |
| Charpy Notched Impact Strength | -40°C | ISO 179/1eA | 12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 17 kJ/m² |
| -40°C | ISO 180/1A | 11 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/MT409AHS NC010 |
|---|---|---|---|
| Odor | VDA270 | 4.00 | |
| Emissions of Organic Compounds | VDA277 | 10.0 µgC/g |
| thermal performance | Test Condition | Test Method | DUPONT USA/MT409AHS NC010 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 187 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1E-04 cm/cm/°C |
| melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-04 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/MT409AHS NC010 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 25 % | |
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 61.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
| flexural modulus | ISO 178 | 2200 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/MT409AHS NC010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| relative permittivity | 100Hz | IEC 60250 | 3.90 |
| Dissipation Factor | 100Hz | IEC 60250 | 6E-03 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 3.70 |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.013 |
| Physical properties | Test Condition | Test Method | DUPONT USA/MT409AHS NC010 |
|---|---|---|---|
| density | ISO 1183 | 1.11 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 1.7 % |
| Ejection Temperature | 190 °C | ||
| shrinkage rate | MD | ISO 294-4 | 1.7 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.90 % |
| flammability | Test Condition | Test Method | DUPONT USA/MT409AHS NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | HB |
| Fogging-G-value | condensate | ISO 6452 | 1E-04 g |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| burning rate | 1.00mm | ISO 3795 | 29 mm/min |