PPS 6165A4-HF2000 JAPAN POLYPLASTIC
DURAFIDE® 
Fiber grade
Glass fiber reinforced、Flame retardant、wear resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodJAPAN POLYPLASTIC/6165A4-HF2000
Charpy Notched Impact Strength23°CISO 179/1eA7.0 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U20 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA7.0 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU20 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A6.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU20 kJ/m²
Supplementary InformationTest ConditionTest MethodJAPAN POLYPLASTIC/6165A4-HF2000
Shrinkage rate内部方法3.18 mm
hardnessTest ConditionTest MethodJAPAN POLYPLASTIC/6165A4-HF2000
Rockwell hardnessM级ASTM D785100
M级ISO 2039-2100
Basic performanceTest ConditionTest MethodJAPAN POLYPLASTIC/6165A4-HF2000
Water absorption rate23℃ISO 620.02 %
Mechanical propertiesTest ConditionTest MethodJAPAN POLYPLASTIC/6165A4-HF2000
Tensile modulusISO 527-2/1A/119000 Mpa
tensile strength 断裂ISO 527-2/1A/5130 Mpa
Impact strength of cantilever beam gap23℃ISO 180/1A6 kJ/m²
tensile strength 断裂,23°CASTM D638131 Mpa
ISO 527-1130 Mpa
bending strengthISO 178210 Mpa
Flexural modulusISO 17818800 Mpa
23°CISO 17818800 Mpa
Rockwell hardnessISO 294-4100 M-scale
Tensile strain断裂ISO 527-2/1A/51.2 %
Tensile modulusISO 527-119000 Mpa
elongation断裂ISO 527-11.2 %
断裂,23°CASTM D6381.3 %
Electrical performanceTest ConditionTest MethodJAPAN POLYPLASTIC/6165A4-HF2000
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 3
Dissipation Factor1kHzASTM D1501E-03
Volume resistivityASTM D2571E+16 ohms·cm
dielectric strengthIEC 60243-125 KV/mm
Volume resistivityIEC 60093>1.0E+17 ohms·cm
dielectric constant1kHzASTM D1505.40
Dissipation Factor1MHzASTM D1509E-04
dielectric constant1MHzASTM D1505.60
relative permittivity1MHzIEC 602505.60
Surface ResistivityIEC 60093>1.0E+15 ohms
Dissipation Factor1MHzIEC 602502E-03
arc resistanceASTM D495182 sec
flammabilityTest ConditionTest MethodJAPAN POLYPLASTIC/6165A4-HF2000
UL flame retardant rating0.75mmUL 94V-0
3.0mmUL 945VA
1.5mmUL 94V-0
Limiting Oxygen IndexISO 4589-253 %
physical property Test ConditionTest MethodJAPAN POLYPLASTIC/6165A4-HF2000
Shrinkage rateISO 25770.2-0.6 %
TDISO 294-40.30-0.70 %
SpecificHeatCapacity of Melt内部方法1600 J/kg/°C
Shrinkage rateMDASTM D9550.10-0.20 %
MDISO 294-40.20-0.60 %
spiral flow length内部方法15.5
Water absorption rate饱和,23°CISO 620.020 %
Shrinkage rateTDASTM D9550.30-0.50 %
densityASTM D7922.00 g/cm³
Specific volumeASTM D7920.502 cm³/g
densityISO 11831.95 g/cm³
melt mass-flow rateASTM D12387.5 g/10min
Thermal performanceTest ConditionTest MethodJAPAN POLYPLASTIC/6165A4-HF2000
Heat distortion temperature1.8MPa,未退火，HDTASTM D648266 °C
melting temperatureISO 11357-3280 °C
Heat distortion temperature1.80Mpa，HDTISO 75-1270 °C
UL flame retardant rating0.750mmUL 94V-0
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A270 °C
Linear coefficient of thermal expansionMDISO 11359-21.9E-05 cm/cm/°C
Heat distortion temperature0.45MPa,退火，HDTASTM D648280 °C
8.0MPa,未退火，HDTISO 75-2/C215 °C
Linear coefficient of thermal expansionTDISO 11359-22.4E-05 cm/cm/°C
Glass Transition TemperatureISO 11357-290.0 °C