PBT B 4500 BASF GERMANY
Ultradur®
film,Pipe fittings
Food contact compliance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | BASF GERMANY/B 4500 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 6.0 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 290 kJ/m² |
hardness | Test Condition | Test Method | BASF GERMANY/B 4500 |
---|---|---|---|
ball-indentation hardness | ISO 2039-1 | 130 Mpa |
Mechanical properties | Test Condition | Test Method | BASF GERMANY/B 4500 |
---|---|---|---|
bending strength | 23°C | ISO 178 | 85.0 Mpa |
tensile strength | 屈服,23°C | ISO 527-2 | 55.0 Mpa |
Tensile strain | 屈服,23°C | ISO 527-2 | 3.7 % |
Tensile creep modulus | 1000hr | ISO 899-1 | 1200 Mpa |
Tensile modulus | 23°C | ISO 527-2 | 2500 Mpa |
Nominal tensile fracture strain | 23°C | ISO 527-2 | >50 % |
Electrical performance | Test Condition | Test Method | BASF GERMANY/B 4500 |
---|---|---|---|
dielectric constant | 100Hz | IEC 60250 | 3.30 |
Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
dielectric constant | 1MHz | IEC 60250 | 3.30 |
Surface Resistivity | IEC 60093 | 1E+13 ohms | |
Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
flammability | Test Condition | Test Method | BASF GERMANY/B 4500 |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | BASF GERMANY/B 4500 |
---|---|---|---|
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.25 % |
饱和,23°C | ISO 62 | 0.50 % | |
density | ISO 1183 | 1.30 g/cm³ | |
Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 19.0 cm3/10min |
Viscosity value | 降低的粘度 | ISO 1628 | 130.0 ml/g |
Thermal performance | Test Condition | Test Method | BASF GERMANY/B 4500 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 165 °C |
Linear coefficient of thermal expansion | MD | 1.4E-04 cm/cm/°C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 65.0 °C |
melting temperature | ISO 3146 | 223 °C |