Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LDPE Unilex™ UP 0100 United Polychem
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | United Polychem/Unilex™ UP 0100 |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | 23℃ | J | 8.19to34.30 |
| hardness | Test Condition | Test Method | United Polychem/Unilex™ UP 0100 |
|---|---|---|---|
| Shore hardness | 23℃ | 49to62 |
| Test Condition | Test Method | United Polychem/Unilex™ UP 0100 | |
|---|---|---|---|
| tear strength | 23℃ | n/m | 3938.05to9380.53 |
| film | Test Condition | Test Method | United Polychem/Unilex™ UP 0100 |
|---|---|---|---|
| fracture | % | 520to920 | |
| MD: Surrender | 8.0to13.24 Mpa | ||
| MD: Fracture | % | 350to910 | |
| 30.0to57.38 Mpa | |||
| MD: Surrender | % | 12to530 | |
| MD | 108.28to230.34 Mpa | ||
| TD: Yield | TD，屈服 | 8.83to13.31 Mpa | |
| Thin film puncture strength | n | 1.5506to3.1685 | |
| fracture | 24.0to50.0 Mpa | ||
| TD | 115.86to291.03 Mpa | ||
| g | 8.0to810 | ||
| kg·m/cm³ | 1182.64 | ||
| TD: Yield | TD，屈服 | % | 4.0to760 |
| yield | 5.2to16.97 Mpa | ||
| MD | kg·m/cm³ | 1116.45 | |
| film thickness | mil | 0.94to2.1 | |
| TD: Fracture | % | 660to920 | |
| MD | g | 0.0to490 | |
| Initial sealing temperature | °C | 99to130 | |
| Thin film puncture strength | kg·m/cm³ | 78.11 | |
| N.m | 347.79 | ||
| TD: Fracture | 18.97to45.17 Mpa |
| Mechanical properties | Test Condition | Test Method | United Polychem/Unilex™ UP 0100 |
|---|---|---|---|
| Flexural modulus | 摩擦系数 | 0.086to0.52 | |
| yield | % | 14to22 | |
| fracture | % | 290to940 | |
| yield | 7.66to17.24 Mpa | ||
| fracture | 9.45to32.69 Mpa | ||
| Flexural modulus | 23℃ | 260.0to271.03 Mpa |
| Electrical performance | Test Condition | Test Method | United Polychem/Unilex™ UP 0100 |
|---|---|---|---|
| dielectric strength | 23℃ | V/mil | 500to760 |
| dielectric constant | 23℃ | 2.10to2.55 | |
| Volume resistivity | 23℃ | ohms·cm | 1.0E+5到1.7E+16 |
| Dissipation Factor | 23℃ | 1.0E-4到3.0E-3 |
| optical performance | Test Condition | Test Method | United Polychem/Unilex™ UP 0100 |
|---|---|---|---|
| transparency | 26.9to95.3 | ||
| transmissivity | % | 68.0to92.3 | |
| gloss | 35to82 | ||
| Haze ratio | % | 0.40to21 |
| physical property | Test Condition | Test Method | United Polychem/Unilex™ UP 0100 |
|---|---|---|---|
| Environmental stress cracking resistance | 23℃ | hr | 0.317to1000 |
| Apparent density | g/cm³ | 0.13to0.56 |