LDPE Polymer-E B231 Asia Polymer Corporation (APC)
--
Film, food packaging
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E B231 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 49 |
| film | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E B231 |
|---|---|---|---|
| tensile strength | TD:断裂,32µm,吹塑薄膜 | ASTM D882 | 19.6 MPa |
| Secant modulus | 1%正割,TD:32µm,吹塑薄膜 | ASTM D882 | 177 MPa |
| Dart impact | 32µm,吹塑薄膜 | ASTM D1709 | 150 g |
| elongation | TD:断裂,32µm,吹塑薄膜 | ASTM D882 | 550 % |
| Elmendorf tear strength | MD:31.8µm | ASTM D1922 | 53.9 kN/m |
| tensile strength | MD:断裂,32µm,吹塑薄膜 | ASTM D882 | 21.6 MPa |
| Elmendorf tear strength | TD:31.8µm | ASTM D1922 | 68.6 kN/m |
| elongation | MD:断裂,32µm,吹塑薄膜 | ASTM D882 | 380 % |
| Secant modulus | 1%正割,MD:32µm,吹塑薄膜 | ASTM D882 | 98.1 MPa |
| Mechanical properties | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E B231 |
|---|---|---|---|
| coefficient of friction | ASTM D1894 | <0.12 |
| optical performance | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E B231 |
|---|---|---|---|
| gloss | 60°,31.8µm,吹塑薄膜 | ASTM D523 | 100 |
| Haze ratio | 31.8µm,吹塑薄膜 | ASTM D1003 | 6.5 % |
| physical property | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E B231 |
|---|---|---|---|
| density | ASTM D1505 | 0.926 g/cm³ | |
| Vinyl acetate content | 内部方法 | 2.5 wt% | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 2.0 g/10min |
| Thermal performance | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E B231 |
|---|---|---|---|
| vicat | ASTM D1525 | 93.0 °C | |
| melting temperature | 内部方法 | 106 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 48.0 °C |
| brittle temperature | ASTM D746 | <-70.0 °C |