PC/ABS C2800 SABIC INNOVATIVE US
CYCOLAC™
Electrical field,Electronic field,Household appliances,Household appliances,Automotive sector
Flame retardant,High mobility,High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/C2800 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 430 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 58.3 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/C2800 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 120 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/C2800 |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 4.8E-03 |
| 60Hz | ASTM D150 | 4.8E-03 | |
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| Volume resistivity | ASTM D257 | 1E+17 ohms·cm | |
| dielectric constant | 50Hz | ASTM D150 | 3.00 |
| Surface Resistivity | ASTM D257 | >1.0E+14 ohms | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| dielectric constant | 100Hz | ASTM D150 | 3.00 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| dielectric strength | 3.20mm,inOil | ASTM D149 | 18 KV/mm |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/C2800 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2690 Mpa | |
| elongation | 断裂 | ASTM D638 | 50 % |
| 屈服 | ASTM D638 | 5.0 % | |
| bending strength | 屈服,100mm跨距 | ASTM D790 | 96.5 Mpa |
| tensile strength | 屈服 | ASTM D638 | 58.6 Mpa |
| Flexural modulus | 100mm跨距 | ASTM D790 | 2690 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/C2800 |
|---|---|---|---|
| UL flame retardant rating | 0.889mm | UL 94 | V-2 |
| 1.47mm | UL 94 | V-0 | |
| 2.31mm | UL 94 | 5VB | |
| Limiting Oxygen Index | ASTM D2863 | 35 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/C2800 |
|---|---|---|---|
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 16 g/10min |
| Water absorption rate | 24hr | ASTM D570 | 0.10 % |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.40-0.60 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.40 % |
| density | -- | ASTM D792 | 1.17 g/cm³ |
| Shrinkage rate | TD:3.20mm | 内部方法 | 0.40-0.60 % |
| density | --1 | ASTM D792 | 1.18 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/C2800 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到60°C | ASTME831 | 7.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 80.0 °C |
| thermal conductivity | ASTMC177 | 0.20 W/m/K | |
| RTI Imp | UL 746 | 70.0 °C | |
| RTI | UL 746 | 80.0 °C | |
| Linear coefficient of thermal expansion | MD:-40到60°C | ASTME831 | 7.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 73.9 °C |
| vicat | ASTM D15257 | 90.6 °C | |
| RTI Elec | UL 746 | 80.0 °C |