Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP G2 U02 102297 LYONDELLBASELL HOLAND
Moplen
Automotive sector、Engine hood parts
High rigidity、High mobility、Anti creep、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL HOLAND/G2 U02 102297 |
|---|---|---|---|
| Flexural modulus | 23℃，正割 | ISO 178 | 4000 Mpa |
| Charpy Notched Impact Strength | 23℃, 铰接断裂 | ISO 179/1eA | 7.0 kJ/m² |
| 23℃, 铰接断裂 | ISO 179/1eU | 38 kJ/m² | |
| Tensile strain | 断裂 | ISO 527-2 | 3.4 % |
| ball-indentation hardness | ISO 2039-1 | 104 Mpa | |
| Tensile modulus | 23℃，正割 | ISO 527-2/1 | 4600 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 75.0 Mpa |
| 屈服 | ISO 527-2 | 72.0 Mpa |
| physical property | Test Condition | Test Method | LYONDELLBASELL HOLAND/G2 U02 102297 |
|---|---|---|---|
| melt mass-flow rate | 230℃/2.16 kg | ISO 1133 | 15 g/10 min |
| Shrinkage rate | 内部方法 | 0.25 - 0.95 % | |
| Melt volume flow rate | 230℃/2.16 kg | ISO 1133 | 17.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/G2 U02 102297 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 155 °C |
| vicat | ISO 306/B50 | 130 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 133 °C |