Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GS-2030MKR MITSUBISHI ENGINEERING JAPAN
IUPILON™
fibre
High mobility,Flame retardant,enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS-2030MKR |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 175 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 8100 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 8700 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 2.0 % |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS-2030MKR |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.05 - 0.25 % | |
| density | ASTM D792/ISO 1183 | 1.43 |
| processability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS-2030MKR |
|---|---|---|---|
| process temperature | 280-300 °C | ||
| Dry conditions | 热风干燥 120℃---約4-8小时 | ||
| screw speed | 50-100 rpm | ||
| Temperature | 80-120 °C |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS-2030MKR |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.8E-05 mm/mm.℃ |