PC/ABS C7230P 5MD018 SABIC INNOVATIVE US
CYCOLAC™
Electronic and electrical、Casters、Household appliances
Aging resistance、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C7230P 5MD018 |
|---|---|---|---|
| Flame Rating | UL 94 | V-0 | |
| Coefficient of Linear Thermal Expansion (Flow) | GB 1040 | 42 µm/m-°C | |
| Vicat Softening Temperature | Rate B/50; ISO 306 | 107 | |
| Deflection Temperature Under Load? (1.8Mpa) | ASTMF1249 | 88 | |
| Vicat Softening Temperature | Rate B/50; ASTM D1525 | 108 | |
| Coefficient of Linear Thermal Expansion (Flow) | ISO 11359-2 | 42 µm/m-°C | |
| Coefficient of Linear Thermal Expansion(Across Flow) | GB 1040 | 49 µm/m-°C | |
| ISO 11359-2 | 59 µm/m-°C | ||
| Vicat Softening Temperature | Equate | 110 | |
| Deflection Temperature Under Load? (1.8Mpa) | Flatw 80*10*4 sp=64mm; ISO 75/Af | 89 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/C7230P 5MD018 |
|---|---|---|---|
| Moisture Absorption | 23°C / 50% RH; ISO 62 | 0.04 % | |
| Modeling Shrinkage (Flow) | SABIC method | 0.0025 - 0.0035 cm/cm | |
| Melt Mass-Flow Rate | ASTM D1238 | @Load 2.16 kg, Temperature 260 | |
| Melt Volume flow Rate | MVR [cm^3/10 min]; ISO 1133 | 49.0 µm/m-°C g/10 min | |
| @Load 2.16 kg, Temperature 260 | |||
| Moisture Absorption (Saturation) | ISO 62 | 0.09 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C7230P 5MD018 |
|---|---|---|---|
| Tensile Elongation (Break) | ISO 178 | 3.8 % | |
| Flexural Modulus | 1.3 mm/min, 50 mm span; ASTM D790 | 4.53 | |
| Tensile Modulus | 1 mm/min; ISO 527 | 5.58 | |
| Notched Izod Impact Strength | ASTM D256 | 0.55 J/cm | |
| Tensile Elongation (Break) | Type I, 50 mm/min; ASTM D638 | 4 % | |
| Notched Izod Impact Strength | 80*10*4; ISO 180/1A | 5 kJ/m² | |
| Flexural Strength | 2 mm/min; ISO 178 | 99 Mpa | |
| Notched Izod Impact Strength | @Temperature -30.0 | ||
| Tensile Strength(Yield) | ISO 178 | 55 Mpa | |
| Flexural Modulus | 2 mm/min; ISO 178 | 4.58 | |
| Tensile Strength(Yield) | Type I, 50 mm/min; ASTM D638 | 58 Mpa | |
| Flexural Strength | 1.3 mm/min, 50 mm span; ASTM D790 | 98 Mpa | |
| Charpy Notched Impact Strength | Edgew 80*10*4 sp=62mm; ISO 179/1eA | 0.5 J/cm² | |
| Tensile Modulus | GB/T 15585-1995 | 5.2 |