PA66 FR70M30V0 DUPONT USA
Zytel®
Fitness equipment、Household appliances、Electronic field、Electrical field
Mineral reinforcement、Antichemical、Flame retardant、Filler: Mineral filler、30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/FR70M30V0 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 2.5 kJ/m² |
| -30°C | ISO 179/1eA | 2.0 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 20 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 20 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/FR70M30V0 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| tensile strength | 断裂 | ISO 527-2 | 73.0 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/FR70M30V0 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| dielectric strength | IEC 60243-1 | 40 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 4.10 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.014 |
| relative permittivity | 1MHz | IEC 60250 | 3.70 |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.014 |
| flammability | Test Condition | Test Method | DUPONT USA/FR70M30V0 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| 0.75mm | IEC 60695-11-10,-20 | V-2 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| FMVSS flammability | FMVSS302 | DNI | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | DUPONT USA/FR70M30V0 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.0 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 4.0 % |
| Shrinkage rate | MD | ISO 294-4 | 1.0 % |
| Ejection Temperature | 210 °C | ||
| MediumDensity | 1.40 g/cm³ | ||
| density | ISO 1183 | 1.62 g/cm³ | |
| SpecificHeatCapacity of Melt | 1700 J/kg/°C | ||
| ThermalConductivityofMelt | 0.23 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.3 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/FR70M30V0 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 263 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 238 °C |
| vicat | ISO 306/B50 | 235 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 145 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.4E-05 cm/cm/°C |
| TD | ISO 11359-2 | 8.1E-05 cm/cm/°C |