PP Homopolymer RIALGLASS H 15 S 30 G RIALTI ITALY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | RIALTI ITALY/RIALGLASS H 15 S 30 G |
|---|---|---|---|
| Impact strength of cantilever beam gap | -20°C | ISO 180/1A | 7.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.0 kJ/m² |
| hardness | Test Condition | Test Method | RIALTI ITALY/RIALGLASS H 15 S 30 G |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒 | ISO 868 | 85 |
| Mechanical properties | Test Condition | Test Method | RIALTI ITALY/RIALGLASS H 15 S 30 G |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 6200 MPa |
| tensile strength | 断裂,23°C | ISO 527-2/20 | 81.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/20 | 4.0 % |
| bending strength | 23°C | ISO 178 | 125 MPa |
| flammability | Test Condition | Test Method | RIALTI ITALY/RIALGLASS H 15 S 30 G |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| physical property | Test Condition | Test Method | RIALTI ITALY/RIALGLASS H 15 S 30 G |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.30 % | |
| ash content | ISO 3451 | 30 % | |
| density | ISO 1183 | 1.12 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 1.0 g/10min |
| Thermal performance | Test Condition | Test Method | RIALTI ITALY/RIALGLASS H 15 S 30 G |
|---|---|---|---|
| ball-indentation hardness | 125°C | IEC 335 | 通过 |
| vicat | ISO 306/B50 | 135 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 150 °C |