Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RFL36XXY-BK1A843 SABIC INNOVATIVE NANSHA
LNP™ LUBRICOMP™
Car hood、Automotive External Parts、Electronic and Electrical、Plastic bag、Architectural Application、Electrical appliances、Lighting applications、sporting goods、medical care
wear resistant、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/RFL36XXY-BK1A843 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 51 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.89 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| -40°C | ISO 180/1A | 7.0 kJ/m² | |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 10.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/RFL36XXY-BK1A843 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9800 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 138 Mpa |
| 断裂 | ASTM D638 | 139 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 12.0 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 9740 Mpa |
| Tensile modulus | ASTM D638 | 11200 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.1 % |
| bending strength | ISO 178 | 211 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.46 |
| Flexural modulus | ISO 178 | 9700 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.1 % |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.59 |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 236 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/RFL36XXY-BK1A843 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.32 % |
| MD：24小时 | ASTM D955 | 0.50 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.62 % |
| Shrinkage rate | TD：24hr | ASTM D955 | 1.1 % |
| TD:24小时 | ISO 294-4 | 1.2 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/RFL36XXY-BK1A843 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 5.5E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 5.5E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 3.8E-05 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 3.8E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 248 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 249 °C |