Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PS POLYREX® PH-88S CHI MEI CORPORATION
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-88S |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.00mm | ASTM D256 | 110 J/m |
| 23°C,3.00mm | ASTM D256 | 150 J/m |
| hardness | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-88S |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 50 |
| Mechanical properties | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-88S |
|---|---|---|---|
| tensile strength | 3.00mm | ASTM D638 | 25.5 MPa |
| bending strength | 6.00mm | ASTM D790 | 35.3 MPa |
| Flexural modulus | 6.00mm | ASTM D790 | 1860 MPa |
| elongation | 断裂,3.00mm | ASTM D638 | 55 % |
| flammability | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-88S |
|---|---|---|---|
| UL flame retardant rating | 1.60mm | UL 94 | HB |
| physical property | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-88S |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 2.6 g/10min |
| density | ASTM D792 | 1.05 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 8.5 g/10min |
| Thermal performance | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-88S |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 80.0 °C |
| 1.8MPa,退火，HDT | ASTM D648 | 94.0 °C | |
| vicat | ASTM D15255 | 100 °C |