Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT HX6600HP 8H4D023 SABIC INNOVATIVE US
XENOY™
Automotive Applications
High mobility、High impact resistance、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HX6600HP 8H4D023 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 1E-04 cm/cm/°C |
| MD：23to60°C | ISO11359-2 | 1.3E-04 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 60.0 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 117 °C |
| Linear thermal expansion coefficient | MD：-40to40°C | ISO11359-2 | 1E-04 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 95.0 °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 60.0 °C | |
| Vicat Softening Temperature | ASTMD152510 | 117 °C | |
| -- | ISO306/B120 | 120 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/HX6600HP 8H4D023 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.050 % |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 10.0 cm3/10min |
| Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 11 g/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 1.2to1.6 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.40 % |
| Melt Viscosity | 260°C,1500sec^-1 | ISO11443 | 210 Pa·s |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HX6600HP 8H4D023 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 1900 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 37.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 150 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 100 % |
| Tensile Modulus | ISO527-2/1 | 1900 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 43.0 Mpa |
| Flexural Modulus | ISO178 | 1800 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 43.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 4.0 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 44.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 4.0 % |
| Flexural Strength | ISO178 | 64.0 Mpa | |
| Tensile Modulus | ASTMD638 | 1900 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 35.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HX6600HP 8H4D023 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 20 kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 100 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 70 kJ/m² |
| -40°C | ISO180/1U | NoBreak | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 65 kJ/m² |
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 100 J |