PC XANTAR® 17 R Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 17 R |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/4A | 60 kJ/m² |
| hardness | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 17 R |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 70 |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 17 R |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric strength | IEC 60243-1 | 29 kV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 6.6E-04 |
| relative permittivity | 100Hz | IEC 60250 | 3.00 |
| 1MHz | IEC 60250 | 2.90 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 9.2E-03 |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 17 R |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | >50 % | |
| Tensile modulus | ISO 527-2 | 2300 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 6.0 % |
| tensile strength | 屈服 | ISO 527-2 | 60.0 MPa |
| Flexural modulus | ISO 178 | 2400 MPa | |
| bending strength | ISO 178 | 90.0 MPa |
| optical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 17 R |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 17 R |
|---|---|---|---|
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | V-2 |
| Limiting Oxygen Index | ISO 4589-2 | 26 % |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 17 R |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.60 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 29.0 cm³/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| density | ISO 1183 | 1.20 g/cm³ | |
| LimitingViscosity | ISO 1628-4 | 42.0 cm³/g | |
| ThermalConductivityofMelt | 0.24 W/m/K |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 17 R |
|---|---|---|---|
| vicat | ISO 306/B50 | 145 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 130 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |