Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS+PA SCHULABLEND® (ABS/PA) M/MK A SCHULMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/SCHULABLEND® (ABS/PA) M/MK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 80 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 22 kJ/m² |
| hardness | Test Condition | Test Method | A SCHULMAN USA/SCHULABLEND® (ABS/PA) M/MK |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 85.0 MPa |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/SCHULABLEND® (ABS/PA) M/MK |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 3.4 % |
| Tensile modulus | ISO 527-2/1A/1 | 1700 MPa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 39.0 MPa |
| flammability | Test Condition | Test Method | A SCHULMAN USA/SCHULABLEND® (ABS/PA) M/MK |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 650 °C |
| physical property | Test Condition | Test Method | A SCHULMAN USA/SCHULABLEND® (ABS/PA) M/MK |
|---|---|---|---|
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 11.0 cm³/10min |
| density | ISO 1183/A | 1.08 g/cm³ |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/SCHULABLEND® (ABS/PA) M/MK |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 66.0 °C |
| vicat | -- | ISO 306/A50 | 204 °C |
| -- | ISO 306/B50 | 120 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 87.0 °C |
Contact Us
Get App
Top