PP PM822V SUNALLOMER JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SUNALLOMER JAPAN/PM822V |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 83 |
| Flexural modulus | ASTM D790/ISO 178 | 1250(MPa) kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 1873-2 | 1100 Mpa | |
| Impact strength of cantilever beam gap | 0℃ | ISO 1873-2 | 1.4 kJ/m² |
| Flexural modulus | ISO 1873-2 | 1250 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 1100(MPa) kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 23℃ | ISO 1873-2 | 5.3 kJ/m² |
| tensile strength | 断裂 | ISO 1873-2 | 32 Mpa |
| Rockwell hardness | ASTM D785 | 83 | |
| Tensile strain | 断裂 | ISO 1873-2 | > 400 % |
| optical performance | Test Condition | Test Method | SUNALLOMER JAPAN/PM822V |
|---|---|---|---|
| gloss | 60° | JIS Z8741 | 88 |
| Physical properties | Test Condition | Test Method | SUNALLOMER JAPAN/PM822V |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 0.9 |
| physical property | Test Condition | Test Method | SUNALLOMER JAPAN/PM822V |
|---|---|---|---|
| melt mass-flow rate | 230℃/2.16 kg | ISO 1873-2 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | SUNALLOMER JAPAN/PM822V |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 1873-2 | 81 °C |