PC EXL1414 WH9A320 SABIC INNOVATIVE NANSHA
LEXAN™ 
Bottle cap、Home appliance components、Electrical applications
Processability、Moderate liquidity、Ductility、copolymer、Good demolding performanc
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Dart impact23°C,TotalEnergyASTM D376370.0 J
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap23°CASTM D256870 J/m
-30°CASTM D256770 J/m
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Charpy Notched Impact Strength-30°CISO 179/1eA65 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A60 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Impact strength of cantilever beam gap23°CISO 180/1A70 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Rockwell hardnessL计秤ASTM D78589
R计秤ASTM D785121
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Dissipation Factor100HzASTM D1501.2E-03
Volume resistivityASTM D257>1.0E+15 ohms·cm
Dissipation Factor1MHzASTM D1509.3E-03
Surface ResistivityASTM D257>1.0E+15 ohms
dielectric constant1MHzASTM D1502.64
100HzASTM D1502.68
dielectric strength0.800mm,inOilASTM D14916 KV/mm
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Tensile modulusISO 527-2/12150 Mpa
elongation屈服ASTM D6386.0 %
tensile strength 断裂ASTM D63850.3 Mpa
Tensile strain屈服ISO 527-2/506.0 %
tensile strength 断裂ISO 527-2/5060.0 Mpa
Flexural modulus50.0mm跨距ASTM D7902230 Mpa
tensile strength 屈服ISO 527-2/5057.0 Mpa
Tensile modulusASTM D6382020 Mpa
elongation断裂ASTM D63898 %
bending strength屈服,50.0mm跨距ASTM D79092.4 Mpa
ISO 17885.0 Mpa
Flexural modulusISO 1782250 Mpa
tensile strength 屈服ASTM D63855.5 Mpa
Tensile strain断裂ISO 527-2/50120 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Burning wire flammability index0.8mmIEC 60695-2-12850 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13875 °C
1.0mmIEC 60695-2-13875 °C
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
UL flame retardant rating0.40mmUL 94HB
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Shrinkage rateMD：3.20mm内部方法0.40-0.80 %
Water absorption rate平衡,23°C,50%RHISO 620.15 %
Shrinkage rateTD：3.20mm内部方法0.40-0.80 %
Melt volume flow rate300°C/1.2kgISO 11339.00 cm3/10min
Water absorption rate饱和,23°CISO 620.35 %
densityASTM D7921.18 g/cm³
ISO 11831.19 g/cm³
melt mass-flow rate300°C/1.2kgASTM D123810 g/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Heat distortion temperature0.45MPa,Unannealed,100mmSpan，HDTISO 75-2/Be140 °C
Linear coefficient of thermal expansionMD：-40到40°CASTME8317E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,3.20mm，HDTASTM D648139 °C
vicatASTM D152510145 °C
Heat distortion temperature1.8MPa,Unannealed,100mmSpan，HDTISO 75-2/Ae128 °C
RTI StrUL 746125 °C
vicat--ISO 306/B120146 °C
Linear coefficient of thermal expansionTD：-40到40°CASTME8317.5E-05 cm/cm/°C
vicat--ISO 306/B50145 °C
Linear coefficient of thermal expansionMD：23到80°CISO 11359-27.2E-05 cm/cm/°C
RTI ImpUL 746120 °C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27.2E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,3.20mm，HDTASTM D648124 °C
ball-indentation hardness125°CIEC 60695-10-2Pass
RTI ElecUL 746130 °C