Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA/ABS M/MK A SCHULMAN USA
SCHULABLEND®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | A SCHULMAN USA/M/MK |
|---|---|---|---|
| Ball Pressure Test | H358/30 | ISO 2039-1 | 85.0 Mpa |
| thermal performance | Test Condition | Test Method | A SCHULMAN USA/M/MK |
|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火 | ISO 75-2/Af | 66.0 °C |
| 0.45MPa,未退火 | ISO 75-2/Bf | 87.0 °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 120 °C |
| -- | ISO 306/A50 | 204 °C |
| mechanical properties | Test Condition | Test Method | A SCHULMAN USA/M/MK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 1700 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 3.4 % |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 39.0 Mpa |
| Physical properties | Test Condition | Test Method | A SCHULMAN USA/M/MK |
|---|---|---|---|
| Melt Volume Flow Rate (MVR) | 250°C/5.0kg | ISO 1133 | 11.0 cm3/10min |
| impact performance | Test Condition | Test Method | A SCHULMAN USA/M/MK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| flammability | Test Condition | Test Method | A SCHULMAN USA/M/MK |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 650 °C |
| 1.5mm | IEC 60695-2-12 | 650 °C | |
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB |