PBT+PET POCAN® ECO T 3240 000000 德国朗盛
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3240 000000 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 60 kJ/m² |
| 23°C | ISO 180/1U | 55 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | <10 kJ/m² |
| -30°C | ISO 179/1eA | <10 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | <10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | <10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 65 kJ/m² |
| Supplementary Information | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3240 000000 |
|---|---|---|---|
| ISO Shortcut | ISO 7792 | PBT+PET.GHMR.09-160.GF45 |
| Mechanical properties | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3240 000000 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 1.9 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 160 MPa |
| Bending Strain | 23°C | 2.1 % | |
| Tensile modulus | 23°C | ISO 527-2/1 | 16000 MPa |
| Flexural modulus | 23°C | ISO 178/A | 15500 MPa |
| bending strength | 23°C | ISO 178 | 260 MPa |
| Electrical performance | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3240 000000 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| physical property | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3240 000000 |
|---|---|---|---|
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
| density | 23°C | ISO 1183 | 1.69 g/cm³ |
| Shrinkage rate | MD:270°C,2.00mm2 | ISO 294-4 | 0.20 % |
| Apparent density | ISO 60 | 0.80 g/cm³ | |
| Shrinkage rate | TD:270°C,2.00mm2 | ISO 294-4 | 0.80 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 30.0 cm³/10min |
| Shrinkage rate | MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
| Thermal performance | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3240 000000 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225to250 °C | |
| MD：23到55°C | ISO 11359-2 | 2E-05 cm/cm/°C | |
| vicat | ISO 306/B120 | 210 °C | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C |
| TD：23to55°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 225 °C |