Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DL-0029E BK1B491 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical Applications,Automotive components,Engine parts
Thermal stability,High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DL-0029E BK1B491 |
|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火,3.20mm | ASTM D648 | 130 °C |
| 0.45MPa,未退火,3.20mm | ASTM D648 | 141 °C | |
| Linear coefficient of thermal expansion | TD：-30to30°C | ASTM D696 | 7.5E-05 cm/cm/°C |
| MD：-30到30°C | ASTM D696 | 7.1E-05 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DL-0029E BK1B491 |
|---|---|---|---|
| Bending modulus | 50.0mm跨距4 | ASTM D790 | 2330 Mpa |
| -- | ASTM D790 | 2340 Mpa | |
| bending strength | ASTM D790 | 86.2 Mpa | |
| elongation | 断裂 | ASTM D638 | 26 % |
| 断裂3 | ASTM D638 | 33 % | |
| 屈服 | ASTM D638 | 5.7 % | |
| Friction coefficient | Dynamic | ASTM D3702Modified | 0.20 |
| Static | ASTM D3702Modified | 0.14 | |
| Tensile modulus | ASTM D638 | 2250 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 56.0 Mpa |
| 断裂3 | ASTM D638 | 47.0 Mpa | |
| 断裂 | ASTM D638 | 51.7 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 55.0 10^-10in^5-min/ft-lb-hr |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DL-0029E BK1B491 |
|---|---|---|---|
| Shrinkage rate | TD：24hr | ASTM D955 | 0.80-1.0 % |
| MD：24小时 | ASTM D955 | 0.60-0.80 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.017 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/DL-0029E BK1B491 |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 46.5 J |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/DL-0029E BK1B491 |
|---|---|---|---|
| UL flame retardant rating | 1.9mm | UL 94 | V-0 |