Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 357X-1001 SABIC INNOVATIVE US
VALOX™
Electrical appliances、Casters、Household goods
Flame retardant、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/357X-1001 |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 85.0 °C | |
| Thermal Conductivity | ISO8302 | 0.17 W/m/K | |
| RTIElec | UL746 | 120 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Flow:23 to 80°C | ISO11359-2 | 1E-04 cm/cm/°C | |
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 130 °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 85.0 °C | |
| RTI | UL746 | 140 °C | |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 130 °C | |
| 0.45MPa, Unannealed,100mm Span | ISO75-2/Be | 135 °C | |
| Flow:-40 to 40°C | ASTME831 | 8.4E-05 cm/cm/°C | |
| Evolution Calendar intelligent importer | UL746 | 120 °C | |
| 1.8MPa, Unannealed,100mm Span | ISO75-2/Ae | 85.0 °C |
| Fill Analysis | Test Condition | Test Method | SABIC INNOVATIVE US/357X-1001 |
|---|---|---|---|
| Melt Viscosity | 260°C,1500sec^-1 | ISO11443 | 310 Pa·s |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/357X-1001 |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 115 Mpa |
| Rockwell Hardness | R计秤 | ISO2039-2 | 115 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/357X-1001 |
|---|---|---|---|
| Modeling Shrinkage | MD:3.20mm | 内部方法 | 1.0到1.4 % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Modeling Shrinkage | TD2 | 内部方法 | 0.90到1.8 % |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 8.00 cm3/10min |
| Melt Mass-Flow Rate | 265°C/5.0kg | ASTMD1238 | 13 g/10min |
| 250°C/5.0kg | ASTMD1238 | 9.6 g/10min | |
| Melt Volume flow Rate | 265°C/5.0kg | ISO1133 | 10.0 cm3/10min |
| Modeling Shrinkage | MD1 | 内部方法 | 1.1到1.8 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.50 % |
| Melt Mass-Flow Rate | 266°C/5.0kg | ASTMD1238 | 13 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/357X-1001 |
|---|---|---|---|
| Break | ASTMD638 | 40.0 Mpa | |
| Yield,50.0mm Span | ASTMD790 | 78.0 Mpa | |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 33.0 mg |
| fracture | ISO527-2/50 | 40.0 Mpa | |
| ISO178 | 80.0 Mpa | ||
| ASTMD638 | 2000 Mpa | ||
| fracture | ISO527-2/50 | 30 % | |
| Break | ASTMD638 | 30 % | |
| yield | ISO527-2/50 | 5.0 % | |
| Yield | ASTMD638 | 5.0 % | |
| 50.0mm Span | ASTMD790 | 2100 Mpa | |
| Yield | ASTMD638 | 50.0 Mpa | |
| yield | ISO527-2/50 | 50.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/357X-1001 |
|---|---|---|---|
| ASTMD256 | 500 J/m | ||
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU,ISO179/2U | 无断裂 |
| ISO180/1A | 20 kJ/m² | ||
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU,ISO179/2U | 无断裂 |
| Unnotched Izod Impact Strength | 23°C | ASTMD4812,ISO180/1U | 无断裂 |
| -30°C | ASTMD4812,ISO180/1U | 无断裂 | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 35.0 J |
| ISO179/2C | 40 kJ/m² | ||
| ISO179/1eA | 45 kJ/m² | ||
| ISO179/1eA,ISO179/2C | 20 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/357X-1001 |
|---|---|---|---|
| Flame Rating | 2.50mm | UL94 | 5VA |
| Glow Wire Flammability Index | 1.00mm | IEC60695-2-12 | 960 °C |
| Oxygen Index | ISO4589-2 | 30 % | |
| Flame Rating | 0.750mm | UL94 | V-0 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/357X-1001 |
|---|---|---|---|
| Comparative Tracking Index | 解决方案B | IEC60112 | 100 V |
| 3.20mm,in Oil | IEC60243-1 | 17 KV/mm | |
| IEC60250 | 1.3E-03 | ||
| 0.800mm, in oil | IEC60243-1 | 34 KV/mm | |
| Hot-wire Ignition | HWI | UL746 | PLC 3 |
| ASTMD149 | 17 KV/mm | ||
| High Amp Arc Ignition | HAI | UL746 | PLC 0 |
| Comparative Tracking Index | -- | IEC60112 | 225 V |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 3 |
| 1.60mm,in Oil | IEC60243-1 | 25 KV/mm | |
| Volume Resistivity | ASTMD257,IEC60093 | >1.0E+15 ohms·cm | |
| ASTMD150,IEC60250 | 3.00 | ||
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| ASTMD150 | 0.013 | ||
| Arc Resistance | ASTMD495 | PLC6 | |
| Comparative Tracking Index | CTI | UL746 | PLC 3 |