Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 SP003 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical appliances、Plastic bag
lubrication、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 150 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 134 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 146 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 147 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| Tensile Strain | 屈服 | ISO527-2 | 18 % |
| Tensile Elongation | 断裂 | ASTMD638 | 24 % |
| Flexural Modulus | ASTMD790 | 1380 Mpa | |
| Tensile Stress | 屈服 | ISO527-2 | 38.0 Mpa |
| Tensile Modulus | ISO527-2/1 | 1580 Mpa | |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.23 |
| Tensile Strength | 屈服 | ASTMD638 | 37.9 Mpa |
| Flexural Modulus | ISO178 | 1300 Mpa | |
| Coefficient of Friction | Static | ASTMD3702Modified | 0.14 |
| Tensile Elongation | 屈服 | ASTMD638 | 18 % |
| Specific Wear Rate | ASTMD3702Modified | 13.5 10^-10in^5-min/ft-lb-hr | |
| Tensile Strain | 断裂 | ISO527-2 | 33 % |
| Tensile Stress | 36.0 Mpa | ||
| Flexural Stress | ISO178 | 44.0 Mpa | |
| Tensile Modulus | ASTMD638 | 1380 Mpa | |
| Tensile Strength | 断裂 | 35.2 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.20 % |
| Modeling Shrinkage | MD：24小时 | ASTMD955 | 0.90to1.1 % |
| TD：24hr | 1.8to2.0 % | ||
| TD:24小时 | ISO294-4 | 1.9 % | |
| MD:24小时 | 1.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 5.00 J |
| 23°C | ISO180/1U | 48 kJ/m² | |
| Notched Izod Impact Strength | ISO180/1A | 4.6 kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 7.80 J |