PPA A-1133 WH505 SOLVAY USA
AMODEL®
Shell、Vehicle electronics、Phone、Industrial components、Automotive interior parts、Industrial applications、Metal substitution、Fuel pipeline、Machine/mechanical compon、Application in the automo、Power/Other Tools、Laptop case、Parts under the hood of a
Chemical resistance、Low moisture absorption、Filler: Glass fiber reinf、33% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SOLVAY USA/A-1133 WH505 |
|---|---|---|---|
| Vicat Softening Temperature | 熔融温度 | ISO11357-3 | 313 °C |
| Heat Deflection Temperature | 1.80MPa退火 | ISO75-2/Af | 280 °C |
| Physical | Test Condition | Test Method | SOLVAY USA/A-1133 WH505 |
|---|---|---|---|
| Density / Specific Gravity | ISO1183 | 1.48 g/cm³ |
| Mechanical Properties | Test Condition | Test Method | SOLVAY USA/A-1133 WH505 |
|---|---|---|---|
| Tensile Elongation?(Break) | 23°C | ISO527-2 | 2.5 % |
| Flexural Strength | 23°C | ISO178 | 319 Mpa |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 49 kJ/m² |
| Flexural Modulus | 23°C | ISO178 | 11600 Mpa |
| Tensile Strength | 23°C | ISO527-2 | 233 Mpa |
| Tensile Modulus | 23°C | ISO527-2 | 13400 Mpa |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 8.8 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 9.5 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 73 kJ/m² |
| Flammability | Test Condition | Test Method | SOLVAY USA/A-1133 WH505 |
|---|---|---|---|
| Fire rating | UL-94 | 0.84mm HB |
| Electrical Properties | Test Condition | Test Method | SOLVAY USA/A-1133 WH505 |
|---|---|---|---|
| Insulation strength | 3.20mm | IEC60243-1 | 39 KV/mm |
| Volume Resistivity | IEC60093 | 1E+15 Ω.cm |