PPO GFN30F-873S SABIC INNOVATIVE SHANGHAI
NORYL™
Automotive components,Laptop case
High temperature resistan,Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-873S |
---|---|---|---|
Hot deformation temperature | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 147 °C |
1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 139 °C | |
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8 | ISO 75-2/Af | 139 °C | |
Linear coefficient of thermal expansion | Flow : -40 to 40°C | ISO 11359-2 | 2.3E-5 cm/cm/°C |
Across Flow : -40 to 40°C | ASTM E831 | 7.5E-5 cm/cm/°C | |
Across Flow : -40°C | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
Flow : -40 to 40°C | ASTM E831 | 2.1E-5 cm/cm/°C | |
Vicat softening temperature | -- | ASTM D15259 | 147 °C |
-- | ISO 306/B120 | 149 °C |
mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-873S |
---|---|---|---|
Bending modulus | 50.0 mm Span4 | ASTM D790 | 7200 Mpa |
--5 | ISO 178 | 6800 Mpa | |
bending strength | Yield, 50.0 mm Span4 | ASTM D790 | 160 Mpa |
--5,6 | ISO 178 | 160 Mpa | |
elongation | Break3 | ASTM D638 | 3.0 % |
Break | ISO 527-2/50 | 2.5 % | |
Tensile modulus | --2 | ASTM D638 | 8600 Mpa |
-- | ISO 527-2/1 | 8200 Mpa | |
tensile strength | Break3 | ASTM D638 | 130 Mpa |
Break | ISO 527-2/50 | 110 Mpa |
Physical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-873S |
---|---|---|---|
melt mass-flow rate | 280°C/5.0 kg | ASTM D1238 | 3.2 g/10 min |
Melt Volume Flow Rate (MVR) | 280°C/5.0 kg | ISO 1133 | 2.00 cm3/10min |
Shrinkage rate | 3.20 mm,Flow | Internal Method | 0.10 - 0.40 % |
Water absorption rate | Saturation, 23°C | ISO 62 | 0.10 % |
Equilibrium, 23°C, 50% RH | ISO 62 | 0.040 % |
impact performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-873S |
---|---|---|---|
Dart impact | 23°C, Total Energy | ASTM D3763 | 20.0 J |
Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 590 J/m |
23°C8 | ISO 180/1U | 30 kJ/m² |
injection | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-873S |
---|---|---|---|
Back pressure | 0.300 to 0.700 Mpa | ||
drying temperature | 110 to 120 °C | ||
drying time | 3.0 to 4.0 hr | ||
Mold temperature | 80 to 110 °C | ||
Processing (melt) temperature | 300 to 325 °C | ||
Screw speed | 20 to 100 rpm | ||
Spray nozzle temperature | 300 to 325 °C | ||
Suggested injection volume | 30 to 70 % | ||
Suggested maximum moisture content | 0.020 % | ||
Temperature at the front of the material cylinder | 290 to 325 °C | ||
Temperature at the rear of the barrel | 265 to 315 °C | ||
Temperature in the middle of the barrel | 275 to 320 °C |