PBT 5010GT15 MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Electronic and Electrical Applications
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT15 |
---|---|---|---|
Surface Resistivity | ASTM D257/IEC 60093 | 1.E+15 Ω | |
Volume resistivity | ASTM D257/IEC 60093 | 1.E+14 Ω.cm |
Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT15 |
---|---|---|---|
bending strength | ASTM D790/ISO 178 | 130 kg/cm²(MPa)[Lb/in²] | |
Flexural modulus | ASTM D790/ISO 178 | 5500 kg/cm²(MPa)[Lb/in²] | |
Tensile modulus | ASTM D638/ISO 527 | 5600 kg/cm²(MPa)[Lb/in²] |
other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT15 |
---|---|---|---|
purpose | 15%玻纤增强.抗冲击韧性 |
Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT15 |
---|---|---|---|
Shrinkage rate | ASTM D955 | 0.5 % | |
density | ASTM D792/ISO 1183 | 1.40 | |
melt mass-flow rate | ASTM D1238/ISO 1133 | 20 g/10min | |
Water absorption rate | ASTM D570/ISO 62 | 0.09 % |
Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT15 |
---|---|---|---|
Combustibility (rate) | UL 94 | HB | |
Heat distortion temperature | HDT | ASTM D648/ISO 75 | 207 ℃(℉) |
melting temperature | 224 ℃(℉) |