Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP GA130 TAIWAN POLYPLASTICS
LAPEROS®
Home appliance components、Electrical applications
Low warpage、high strength、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | TAIWAN POLYPLASTICS/GA130 |
|---|---|---|---|
| ColorNumber | VF2201/BK210P |
| Mechanical properties | Test Condition | Test Method | TAIWAN POLYPLASTICS/GA130 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 1.6 % |
| bending strength | ISO 178 | 200 Mpa | |
| Flexural modulus | ISO 178 | 15000 Mpa | |
| Bending Strain | ISO 178 | 1.8 % | |
| tensile strength | ASTM D638 | 150 Mpa |
| Electrical performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/GA130 |
|---|---|---|---|
| Dissipation Factor | 1kHz | IEC 60250 | 0.020 |
| relative permittivity | 1kHz | IEC 60250 | 4.10 |
| dielectric strength | 1.00mm | IEC 60243-1 | 48 KV/mm |
| Dissipation Factor | 耐电弧性 | IEC 60250 | 127 sec |
| Volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 23 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 3.70 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.030 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | TAIWAN POLYPLASTICS/GA130 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TAIWAN POLYPLASTICS/GA130 |
|---|---|---|---|
| Shrinkage rate | TD:1.00mm | 内部方法 | 0.42 % |
| MD:1.00mm | 内部方法 | 0.10 % |
| Thermal performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/GA130 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 300 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 280 °C |