SBS 800S AKelastomers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKelastomers/ 800S |
|---|---|---|---|
| Charpy Notched Impact Strength | 完全断裂 | ISO 179 | 1.1 kJ/m² |
| Impact strength of simply supported beam without notch | 完全断裂 | ISO 179 | 23 kJ/m² |
| hardness | Test Condition | Test Method | AKelastomers/ 800S |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 75 |
| Rockwell hardness | R计秤 | ISO 2039-2 | 78 |
| Mechanical properties | Test Condition | Test Method | AKelastomers/ 800S |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 41.0 MPa |
| Tensile strain | 断裂 | ISO 527-2/5 | 12 % |
| Flexural modulus | ISO 178 | 2250 MPa | |
| bending strength | ISO 178 | 54.0 MPa |
| optical performance | Test Condition | Test Method | AKelastomers/ 800S |
|---|---|---|---|
| transmissivity | 2000µm | ISO 13468 | 90.0 % |
| Haze ratio | 2000µm | ISO 14782 | 3.0 % |
| physical property | Test Condition | Test Method | AKelastomers/ 800S |
|---|---|---|---|
| Shrinkage rate | 0.20to0.80 % | ||
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 6.0 g/10min |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.10 % |
| density | ISO 1183 | 1.02 g/cm³ |
| Thermal performance | Test Condition | Test Method | AKelastomers/ 800S |
|---|---|---|---|
| vicat | ISO 306/A50 | 96.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 69.0 °C |