ABS PA-765A TAIWAN CHIMEI
POLYLAC®
Home appliance components、Fitness equipment、Electronic field、Electrical field
High mobility、Flame retardant
SGS
MSDS
RoHS
UL
UL
UL
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | TAIWAN CHIMEI/PA-765A |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 24 kJ/m² |
Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 230 J/m |
23°C,6.40mm | ASTM D256 | 200 J/m | |
Charpy Notched Impact Strength | -30°C | ISO 179 | 10 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
23°C | ISO 180/1A | 23 kJ/m² |
hardness | Test Condition | Test Method | TAIWAN CHIMEI/PA-765A |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 101 |
Mechanical properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-765A |
---|---|---|---|
tensile strength | 屈服4 | ASTM D638 | 39.1 Mpa |
屈服 | ISO 527-2/50 | 38.0 Mpa | |
elongation | 断裂4 | ASTM D638 | 20 % |
bending strength | --5 | ASTM D790 | 62.5 Mpa |
--6 | ISO 178 | 56.0 Mpa | |
elongation | 断裂 | ISO 527-2/50 | 10 % |
Flexural modulus | --6 | ISO 178 | 1800 Mpa |
--5 | ASTM D790 | 2210 Mpa | |
tensile strength | 断裂 | ISO 527-2/50 | 29.0 Mpa |
flammability | Test Condition | Test Method | TAIWAN CHIMEI/PA-765A |
---|---|---|---|
UL flame retardant rating | 2.5mm | UL 94 | V-0 |
3.0mm | UL 94 | 5VA | |
1.5mm | UL 94 | V-1 |
physical property | Test Condition | Test Method | TAIWAN CHIMEI/PA-765A |
---|---|---|---|
density | 23°C | ISO 1183 | 1.17 g/cm³ |
melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 4.6 g/10min |
Shrinkage rate | ISO 294-4 | 0.30-0.60 % | |
density | --3 | ASTM D792 | 1.17 g/cm³ |
Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 46.0 cm3/10min |
Thermal performance | Test Condition | Test Method | TAIWAN CHIMEI/PA-765A |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTMD648 | 76.0 °C |
1.8MPa,退火,HDT | ASTM D648 | 85.0 °C | |
vicat | -- | ASTM D15257 | 92.0 °C |
-- | ISO 306/A50 | 93.0 °C | |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 84.0 °C |
vicat | -- | ISO 306/B50 | 79.0 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.5E-05 cm/cm/°C |