TP, Unspecified Hapflex™ 565-3 HAPCO USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | HAPCO USA/Hapflex™ 565-3 |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256 | 无断裂 | |
Suspended wall beam without notch impact strength | ASTM D256 | 无断裂 |
hardness | Test Condition | Test Method | HAPCO USA/Hapflex™ 565-3 |
---|---|---|---|
Shore hardness | 邵氏A | ASTM D2240 | 65 |
Mechanical properties | Test Condition | Test Method | HAPCO USA/Hapflex™ 565-3 |
---|---|---|---|
elongation | 断裂 | ASTM D638 | 500 % |
tensile strength | ASTM D638 | 6.21 MPa | |
Tensile modulus | ASTM D638 | 4.14 MPa |
thermosetting | Test Condition | Test Method | HAPCO USA/Hapflex™ 565-3 |
---|---|---|---|
Thermosetting mixed viscosity | 25°C | ASTM D4878 | 670 cP |
GelTime | 25°C | ASTM D2971 | 3.0 min |
stripping time | 21°C | 内部方法 | 30to60 min |
Thermosetting components | 部件A | 按重量计算的混合比:100.按容量计算的混合比:100 | |
部件B | 按重量计算的混合比:100.按容量计算的混合比:100 |
elastomer | Test Condition | Test Method | HAPCO USA/Hapflex™ 565-3 |
---|---|---|---|
tear strength | ASTM D624 | 14.4 kN/m |
physical property | Test Condition | Test Method | HAPCO USA/Hapflex™ 565-3 |
---|---|---|---|
Shrinkage rate | MD | ASTM D2566 | 0.20to0.40 % |
density | ASTM D4669 | 1.05 g/cm³ | |
Weight Percubicinch | 17 g |