Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC FXE1414 WH9D312 SABIC INNOVATIVE NANSHA
LEXAN™
Electrical appliances,Electronic field,Electrical field,Household appliances
Low temperature resistanc,transparent,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/FXE1414 WH9D312 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 70.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 65 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 60 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 70.0 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 70 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/FXE1414 WH9D312 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2150 Mpa | |
| --2 | ASTM D638 | 2020 Mpa | |
| tensile strength | 屈服3 | ASTM D638 | 55.0 Mpa |
| elongation | 断裂3 | ASTM D638 | 98 % |
| 屈服 | ASTM D638 | 6.0 % | |
| 断裂 | ISO 527-2/50 | 120 % | |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 92.0 Mpa |
| --5,6 | ISO 178 | 85.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2230 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 60.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2230 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 57.0 Mpa |
| elongation | 断裂 | ASTM D638 | 98 % |
| 屈服3 | ASTM D638 | 6.0 % | |
| Flexural modulus | ISO 178 | 2250 Mpa | |
| tensile strength | 断裂3 | ASTM D638 | 50.0 Mpa |
| Flexural modulus | --5 | ISO 178 | 2250 Mpa |
| tensile strength | 断裂 | ASTM D638 | 50.3 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Tensile modulus | ASTM D638 | 2020 Mpa | |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 92.4 Mpa |
| elongation | 屈服 | ISO 527-2/50 | 6.0 % |
| bending strength | ISO 178 | 85.0 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 55.5 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| Tensile modulus | -- | ISO 527-2/1 | 2150 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/FXE1414 WH9D312 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.35 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.40 - 0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/FXE1414 WH9D312 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 7.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距9，HDT | ISO 75-2/Ae | 128 °C |
| Linear coefficient of thermal expansion | 横向 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 139 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| vicat | ASTM D152510 | 145 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 139 °C |
| 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 128 °C | |
| vicat | -- | ISO 306/B120 | 146 °C |
| -- | ASTM D152510 | 145 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 145 °C |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 124 °C |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 124 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/FXE1414 WH9D312 |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| drying temperature | 120 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the rear of the barrel | 270 to 295 °C | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 295 to 315 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 70 to 95 °C | ||
| Spray nozzle temperature | 290 to 310 °C |