Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 PrimePart® PLUS PA 2221 EOS GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EOS GmbH/PrimePart® PLUS PA 2221 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C4 | ISO 179/1eU | 35 kJ/m² |
| 23°C2 | ISO 179/1eU | 18 kJ/m² | |
| 23°C2 | ISO 179/1fU | 22 kJ/m² | |
| 23°C3 | ISO 179/1fU | 61 kJ/m² | |
| Charpy Notched Impact Strength | 23°C4 | ISO 179/1eA | 3.9 kJ/m² |
| 23°C2 | ISO 179/1eA | 3.2 kJ/m² |
| hardness | Test Condition | Test Method | EOS GmbH/PrimePart® PLUS PA 2221 |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒 | ISO 868 | 75 |
| Mechanical properties | Test Condition | Test Method | EOS GmbH/PrimePart® PLUS PA 2221 |
|---|---|---|---|
| tensile strength | --2 | ISO 527-2 | 40.0 MPa |
| --4 | ISO 527-2 | 47.0 MPa | |
| bending strength | 8.4%应变3 | ISO 178 | 59.0 MPa |
| Tensile strain | 断裂3 | ISO 527-2 | 16 % |
| Tensile modulus | --2 | ISO 527-2 | 1600 MPa |
| Tensile strain | 断裂2 | ISO 527-2 | 4.0 % |
| Tensile modulus | --3 | ISO 527-2 | 1650 MPa |
| Flexural modulus | 23°C2 | ISO 178 | 1340 MPa |
| bending strength | 8.2%应变2 | ISO 178 | 54.0 MPa |
| Flexural modulus | 23°C3 | ISO 178 | 1390 MPa |
| physical property | Test Condition | Test Method | EOS GmbH/PrimePart® PLUS PA 2221 |
|---|---|---|---|
| density | 内部方法 | 0.970 g/cm³ |
| Thermal performance | Test Condition | Test Method | EOS GmbH/PrimePart® PLUS PA 2221 |
|---|---|---|---|
| melting temperature | ISO 11357 | 187 °C | |
| Heat distortion temperature | 0.45MPa,未退火3，HDT | ISO 75-2/B | 157 °C |
| 0.45MPa,未退火2，HDT | ISO 75-2/B | 148 °C | |
| 1.8MPa,未退火2，HDT | ISO 75-2/A | 69.0 °C | |
| 1.8MPa,未退火4，HDT | ISO 75-2/A | 70.0 °C |