PC 8000-05 LG CHEM KOREA
--
Lighting applications,Electrical applications
high strength,High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/8000-05 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 无断裂 |
| hardness | Test Condition | Test Method | LG CHEM KOREA/8000-05 |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 50 |
| M 计秤 | ISO 2039-2 | 50 | |
| R 计秤 | ISO 2039-2 | 120 | |
| R 级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/8000-05 |
|---|---|---|---|
| tensile strength | 屈服, 23°C2 | ASTM D638 | 58.0 Mpa |
| Tensile modulus | -- | ISO 527-2 | 2390 Mpa |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| tensile strength | 断裂 | ASTM D638 | 68.0 Mpa |
| 断裂 | ISO 527-2 | 64.0 Mpa | |
| Flexural modulus | -- | ISO 178 | 1940 Mpa |
| bending strength | -- | ISO 178 | 82.0 Mpa |
| tensile strength | 屈服, 23°C | ISO 527-2/50 | 57.0 Mpa |
| elongation | 断裂 | ASTM D638 | 120 % |
| bending strength | -- | ASTM D790 | 86.0 Mpa |
| Tensile modulus | -- | ASTM D638 | 2180 Mpa |
| Flexural modulus | -- | ASTM D790 | 2030 Mpa |
| elongation | 断裂 | ISO 527-2 | 110 % |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/8000-05 |
|---|---|---|---|
| Volume resistivity | 23°C | ASTM D257 | 1.0E+15 ohms·cm |
| optical performance | Test Condition | Test Method | LG CHEM KOREA/8000-05 |
|---|---|---|---|
| transmissivity | 3000 µm | ISO 13468-1 | > 88.0 % |
| Haze ratio | 3000 µm | ASTM D1003 | < 1.0 % |
| transmissivity | 3000 µm | ASTM D1003 | > 88.0 % |
| Haze ratio | 3000 µm | ISO 14782 | < 1.0 % |
| physical property | Test Condition | Test Method | LG CHEM KOREA/8000-05 |
|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.12 % |
| 平衡, 23°C, 50% RH | ASTM D570 | 0.20 % | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 3.5 g/10 min |
| Shrinkage rate | Flow | ASTM D955 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/8000-05 |
|---|---|---|---|
| Linear coefficient of thermal expansion | -40 到 82°C，流动 | ASTM D696 | 7.0E-5 cm/cm/°C |
| vicat | ISO 306/B120 | 138 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 115 °C |
| 1.8 MPa, 未退火, 4.00 mm，HDT | ASTM D648 | 118 °C | |
| 1.8 MPa, 退火, 4.00 mm，HDT | ASTM D648 | 130 °C | |
| 0.45 MPa, 退火, 4.00 mm，HDT | ASTM D648 | 132 °C |