Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PFA AP-201 DAIKIN JAPAN
NEOFLON®
Wire sheath
High temperature strength、copolymer、High mobility、Good liquidity、High transparency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DAIKIN JAPAN/AP-201 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | DAIKIN JAPAN/AP-201 |
|---|---|---|---|
| Shore hardness | 邵氏 D邵氏 D | ASTM D2240 | 60 to 70 |
| compressive strength | 1% 应变1% Strain | ASTM D695 | 4.90 to 5.90 Mpa |
| Compression Modulus | ASTM D695 | 490 to 590 Mpa | |
| compressive strength | 25% 应变25% Strain | ASTM D695 | 31.4 to 33.3 Mpa |
| Flexural modulus | ASTM D790 | 580 to 690 Mpa | |
| bending strength | ASTM D790 | No break | |
| Heat distortion temperature | 100℃，6.9 MPa100°C, 6.9 MPa 22，HDT | ASTM D621 | 2.00 to 3.00 % |
| tensile strength | 屈服屈服 | JIS K6891 | 24.5 to 29.4 Mpa |
| Heat distortion temperature | 25℃，14 MPa25°C, 14 MPa 22，HDT | ASTM D621 | 2.50 to 3.00 % |
| 100℃，6.9 MPa100°C, 6.9 MPa 33，HDT | ASTM D621 | 8.50 to 9.50 % | |
| 25℃，14 MPa25°C, 14 MPa 33，HDT | ASTM D621 | 8.00 to 9.00 % | |
| coefficient of friction | 与钢 - 静态与钢 - 静态 | 0.040 to 0.050 | |
| Tensile strain | 断裂断裂 | JIS K6891 | 350 to 450 % |
| Flame retardant performance | Test Condition | Test Method | DAIKIN JAPAN/AP-201 |
|---|---|---|---|
| 1.60 mm??1.6 mm | 1.60mm | UL 94 | V-0 |
| Limiting Oxygen Index | 1.57 mm1.57 mm | ASTM D2863 | > 95 % |
| physical property | Test Condition | Test Method | DAIKIN JAPAN/AP-201 |
|---|---|---|---|
| Apparent density | JIS K6891 | 1.00 to 1.40 g/cm³ | |
| Water absorption rate | 饱和饱和 | ASTM D570 | < 0.010 % |
| density | ASTM D792 | 2.14 - 2.16 g/cm³ | |
| melt mass-flow rate | 372℃，5.0kg372℃/5.0 kg | ASTM D1238 | 20 to 30 g/10min |
| Apparent viscosity | 380℃380℃ | 2.00E+6 - 2.50E+7 mPa·s |
| Thermal performance | Test Condition | Test Method | DAIKIN JAPAN/AP-201 |
|---|---|---|---|
| Specific heat capacity | 1050 J/kg/℃ | ||
| Linear coefficient of thermal expansion | MD：20~100℃MD：20 到 100℃ | ASTM D696 | 0.00012 1/℃ |
| thermal conductivity | ASTM C177 | 0.26 W/m/K | |
| melting temperature | ASTM D4591 | 300 to 310 °C |