PA66 RFL36XXZ-GYMDNAT SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Car hood,Plastic bag,Electrical appliances,Lighting applications,sporting goods
wear resistant,enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RFL36XXZ-GYMDNAT |
|---|---|---|---|
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 5.5E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ASTM E831 | 3.8E-5 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL36XXZ-GYMDNAT |
|---|---|---|---|
| Bending modulus | ISO 178 | 9700 Mpa | |
| bending strength | -- | ASTM D790 | 236 Mpa |
| -- | ISO 178 | 211 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.1 % |
| Friction coefficient | Dynamic | ASTM D3702 | 0.58 |
| tensile strength | 断裂 | ASTM D638 | 139 Mpa |
| 断裂 | ISO 527-2 | 138 Mpa | |
| Wear factor | ASTM D3702 | 2.4E+6 10^-8 mm³/N·m |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/RFL36XXZ-GYMDNAT |
|---|---|---|---|
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 10.0 J |
| -- | ISO 6603-2 | 2.00 J |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/RFL36XXZ-GYMDNAT |
|---|---|---|---|
| Back pressure | 0.200 to 0.300 Mpa | ||
| drying temperature | 80 °C | ||
| drying time | 4.0 hr | ||
| Mold temperature | 95 to 110 °C | ||
| Processing (melt) temperature | 280 to 305 °C | ||
| Screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.15 to 0.25 % | ||
| Temperature at the front of the material cylinder | 295 to 305 °C | ||
| Temperature at the rear of the barrel | 265 to 275 °C | ||
| Temperature in the middle of the barrel | 280 to 295 °C |