PPA T1 GF 30 black (3466) AKRO-PLASTIC GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 30 black (3466) |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| -30°C | ISO 179/1eA | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| -30°C | ISO 179/1eU | 45 kJ/m² |
| Supplementary Information | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 30 black (3466) |
|---|---|---|---|
| ReinforcementContent | ISO 1172 | 30 % |
| hardness | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 30 black (3466) |
|---|---|---|---|
| ball-indentation hardness | H961/30 | ISO 2039-1 | 290 MPa |
| Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 30 black (3466) |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 30 black (3466) |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2/5 | 215 MPa |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.2 % |
| Fracture bending strain | ISO 178 | 3.0 % | |
| Flexural modulus | ISO 178 | 11000 MPa | |
| Tensile modulus | ISO 527-2/1 | 12500 MPa | |
| bending strength | ISO 178 | 300 MPa |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 30 black (3466) |
|---|---|---|---|
| burning rate | 1.00mm | FMVSS302 | <100 mm/min |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 30 black (3466) |
|---|---|---|---|
| spiral flow length | 内部方法 | 73.0 cm | |
| density | 23°C | ISO 1183 | 1.40 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 0.90 % |
| MD | ISO 294-4 | 0.40 % | |
| Water absorption rate | 70°C | ISO 1110 | 1.3 % |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 30 black (3466) |
|---|---|---|---|
| TemperatureIndex | 50%LossofTensileStrength,20000hr | IEC 216 | 150to160 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 310 °C |
| melting temperature | DIN EN11357-1 | 313 °C | |
| TemperatureIndex | 50%LossofTensileStrength,5000hr | IEC 216 | 170to180 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 285 °C |
| 8.0MPa,未退火，HDT | ISO 75-2/C | 165 °C |