PS TOTAL Polystyrene Compound 807 法国TOTAL石化
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 807 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 807 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 25.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 39 % |
| tensile strength | 屈服 | ISO 527-2 | 27.0 MPa |
| Flexural modulus | ISO 178 | 2400 MPa |
| flammability | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 807 |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 960 °C | |
| UL flame retardant rating | 1.6mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 807 |
|---|---|---|---|
| Apparent density | 0.60 g/cm³ | ||
| Shrinkage rate | 0.40to0.70 % | ||
| density | 23°C | ISO 1183 | 1.04 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 14 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | <0.10 % |
| Thermal performance | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 807 |
|---|---|---|---|
| vicat | ISO 306/B50 | 87.0 °C |