Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT B3235 LANXESS GERMANY
Pocan®
Fiber grade,Automotive sector,Electrical field,Electronic field
Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | LANXESS GERMANY/B3235 |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 4 | |
| Volume resistivity | ASTM D257/IEC 60093 | ＞1013 Ω.cm |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/B3235 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 65 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 200 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 8000 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 10000 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | ＜10 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 2.5 % | |
| tensile strength | ASTM D638/ISO 527 | 140 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | LANXESS GERMANY/B3235 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.3/1.2 % | |
| density | ASTM D792/ISO 1183 | 1.55 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 13 g/10min |
| processability | Test Condition | Test Method | LANXESS GERMANY/B3235 |
|---|---|---|---|
| Melt Temperature | 225 °C |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/B3235 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 210 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 215 ℃（℉） |