Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-764B TAIWAN CHIMEI
POLYLAC®
Home appliance components、Fitness equipment、Electronic field、Electrical field
heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-764B |
|---|---|---|---|
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 101（214） ℃（℉） | |
| Burning Rate | UL94 | 2.5mm，V-0 3.2mm，5VA | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | - mm/mm.℃ | |
| Heat Deflection Temperature | ASTM D648/ISO 75 | 80（176） ℃（℉） |
| Mechanical Properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-764B |
|---|---|---|---|
| Flexural Strength | ASTM D790/ISO 178 | 660（9，370） kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | - % | |
| Rockwell Hardness | ASTM D785 | R-102 | |
| Tensile Strength | ASTM D638/ISO 527 | 400（5，810） kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in | |
| Izod notch impact strength | ASTM D256/ISO 179 | 16（3.0） kg·cm/cm(J/M)ft·lb/in | |
| Tensile Modulus | ASTM D638/ISO 527 | - kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ASTM D638/ISO 527 | 20 % | |
| Flexural Modulus | ASTM D790/ISO 178 | 23000（32000） kg/cm²(MPa)[Lb/in²] |
| Other | Test Condition | Test Method | TAIWAN CHIMEI/PA-764B |
|---|---|---|---|
| Color | - | ||
| purpose | 计算机配件 / 电子产品零配件 / 电动工具零配件 / 电视机外壳 / 事务机器等 | ||
| Remarks | 在射出周期中勿将热融胶长期停留在加热管中 | ||
| characteristic | 难燃性 耐光性 耐热性 |
| Physical Properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-764B |
|---|---|---|---|
| Melt Mass-Flow Rate | ASTM D1238/ISO 1133 | 28 g/10min | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | - % | |
| Density | ASTM D792/ISO 1183 | 1.16 | |
| Modeling Shrinkage | ASTM D955 | - % |
| Processing | Test Condition | Test Method | TAIWAN CHIMEI/PA-764B |
|---|---|---|---|
| Screw Speed | - rpm | ||
| Drying conditions | 80°C下烘料约2~3小时 | ||
| Melt Temperature | - °C | ||
| Processing temperature | 180~220°C °C | ||
| Mold Temperature | 40~70°C °C | ||
| Pressure | 50~80kg/cm² Mpa |